Rubber composition, and conveyor belt using the same

{
  "publication_number": "US12173144B2",
  "country": "US",
  "kind": "B2",
  "title": "Rubber composition, and conveyor belt using the same",
  "abstract": "The present invention discloses a rubber composition comprising, in parts by weight, 100 parts of a rubber matrix, 1.5 to 9 parts of a crosslinking agent, 0.2 to 9 parts of an assistant crosslinking agent, 40 to 170 parts of a reinforcing filler, 6 to 93 parts of a plasticizer and 3 to 25 parts of a metal oxide. The rubber matrix comprises a branched polyethylene with a content represented as A, in which 0<A≤100 parts, an EPM with a content represented as B, in which 0≤B<100 parts, and an EPDM with a content represented as C, in which 0≤C<100 parts. The present invention provides a rubber composition which is excellent in heat resistance and mechanical properties and is useful in a cover rubber of a conveyor belt.",
  "claims": [
    "1. A conveyor belt, comprising a working face cover rubber, a non-working face cover rubber, and a tensile layer being provided between the working face cover rubber and the non-working face cover rubber, wherein at least one of the working face cover rubber and the non-working face cover rubber comprises rubber compound formed from a rubber composition comprising a rubber matrix and essential components, wherein, based on 100 parts by weight of the rubber matrix, the rubber matrix comprises, a branched polyethylene with a content represented as A, in which 0<A≤100 parts, an EPM with a content represented as B, in which 0≤B<100 parts, and an EPDM with a content represented as C, in which 0≤C<100 parts; wherein based on 100 parts by weight of the rubber matrix, the essential components comprise 1.5-9 parts of a crosslinking agent, 0.2-9 parts of an assistant crosslinking agent, 40-170 parts of a reinforcing filler, 6-93 parts of a plasticizer, and 3-25 parts of a metal oxide, and wherein the branched polyethylene comprises an ethylene homopolymer having a branching degree of from about 60 to 99 branches/1000 carbon atoms, a weight average molecular weight of from 66,000 to 518,000, and a Mooney viscosity ML (1+4) at 125° C. of from 6 to 102.",
    "2. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of from 60 to 94 branches/1000 carbon atoms.",
    "3. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of from 60 to 90 branches/1000 carbon atoms.",
    "4. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of from 60 to 87 branches/1000 carbon atoms.",
    "5. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of from 60 to 82 branches/1000 carbon atoms.",
    "6. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of from 60 to 70 branches/1000 carbon atoms.",
    "7. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of 60 branches/1000 carbon atoms, 70 branches/1000 carbon atoms, 82 branches/1000 carbon atoms, 87 branches/1000 carbon atoms, 90 branches/1000 carbon atoms, 94 branches/1000 carbon atoms, or 99 branches/1000 carbon atoms.",
    "8. The conveyor belt according to claim 1, wherein the ethylene homopolymer has a branching degree of about 60 branches/1000 carbon atoms, about 70 branches/1000 carbon atoms, about 82 branches/1000 carbon atoms, about 87 branches/1000 carbon atoms, about 90 branches/1000 carbon atoms, 94 branches/1000 carbon atoms, or 99 branches/1000 carbon atoms.",
    "9. The conveyor belt according to claim 1, wherein the rubber matrix comprises, in parts by weight, 100 parts of the branched polyethylene; and based on 100 parts by weight of the rubber matrix, the essential components comprise 1.5 to 9 parts of a crosslinking agent, 0.2-9 parts of an assistant crosslinking agent, 40 to 170 parts of a reinforcing filler, 6-93 parts of a plasticizer, and 3-25 parts of a metal oxide.",
    "10. The conveyor belt according to claim 1, wherein, in 100 parts by weight of the rubber matrix, the content of the branched polyethylene is represented as A, in which 10≤A≤100 parts, the content of the EPM is represented as B, in which 0≤B≤90 parts, and the content of the EPDM is represented as C, in which 0≤C≤90 parts.",
    "11. The conveyor belt according to claim 1, wherein, the rubber composition further comprises, based on 100 parts by weight of the rubber matrix, 1 to 3 parts of a stabilizer, 1 to 5 parts of polyethylene glycol, and 0 to 3 parts of a vulcanization accelerator.",
    "12. The conveyor belt according to claim 11, wherein, the stabilizer comprises at least one of 2,2,4-trimethyl-1,2-dihydroquinoline polymer (RD), 6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline (AW), and 2-mercaptobenzimidazole (MB).",
    "13. The conveyor belt according to claim 11, wherein, the polyethylene glycol comprises at least one of those polyethylene glycol having a molecular weight of 2000, 3400, and 4000.",
    "14. The conveyor belt according to claim 11, wherein, the vulcanization accelerator comprises at least one of 2-mercaptobenzothiazole, dibenzothiazyl disulfide, tetramethyl thiuram monosulfide, tetramethyl thiuram disulfide, tetraethyl thiuram disulfide, N-cyclohexyl-2-benzothiazole sulfenamide, N,N-dicyclohexyl-2-benzothiazole sulfenamide, bismaleimide, and ethylene thiourea.",
    "15. The conveyor belt according to claim 1, wherein, the crosslinking agent comprises a peroxide crosslinking agent and sulfur, wherein, the peroxide crosslinking agent comprises at least one of di-tert-butyl peroxide, dicumyl peroxide, tert-butyl cumyl peroxide, 1,1-di-tert-butyl peroxide-3,3,5-trimethylcyclohexane, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexane, 2,5-dimethyl-2,5-di(tert-butylperoxy)hexyne-3, bis(tert-butylperoxyisopropyl)benzene, 2,5-dimethyl-2,5-bis(benzoylperoxy)hexane, tert-butyl peroxybenzoate, and tert-butylperoxy-2-ethylhexyl carbonate.",
    "16. The conveyor belt according to claim 1, wherein, the assistant crosslinking agent comprises at least one of triallyl cyanurate, triallyl isocyanurate, ethylene glycol dimethacrylate, triethylene glycol dimethacrylate, triallyl trimellitate, trimethylolpropane trimethacrylate, N,N′-m-phenylene bismaleimide, N,N′-bis(furfurylidene) acetone, 1,2-polybutadiene, a metal salt of an unsaturated carboxylic acid, and sulfur.",
    "17. The conveyor belt according to claim 1, wherein, the plasticizer comprises at least one of stearic acid, pine tar, motor oil, naphthenic oil, paraffin oil, coumarone, paraffin, liquid polyisobutene, and dioctyl sebacate; the metal oxide comprises at least one of zinc oxide and magnesia; the reinforcing filler comprises at least one of carbon black, calcium carbonate, calcined clay, magnesium silicate, aluminum silicate, and magnesium carbonate.",
    "18. The conveyor belt according to claim 1, wherein, the conveyor belt is a cold resistant conveyor belt, which comprises a working face cover rubber, a non-working face cover rubber and a tensile layer being provided between the working face cover rubber and the non-working face cover rubber, wherein, the rubber compound used for the working face cover rubber comprises the rubber composition, and the plasticizer in the rubber composition comprises a cold-resistant plasticizer.",
    "19. The conveyor belt according to claim 1, wherein, the conveyor belt is a static-conducting conveyor belt, which comprises an inner cover rubber, an outer cover rubber, and a tensile layer being provided between the inner cover rubber and the outer cover rubber, wherein, the rubber compound used for at least one of the inner cover rubber and the outer cover rubber comprises the rubber composition, and the reinforcing filler in the rubber composition comprises at least one of conductive carbon black and graphite powder."
  ],
  "description_excerpt": "The present invention relates to the technical field of rubbers, in particular to a rubber composition, and a processing method thereof, and further to a conveyor belt using the rubber composition and a production method thereof.\n\nIn order to meet the high temperature resistance requirement, the rubber compound is partially or fully an ethylene-propylene rubber of high heat resistance in various portions (especially the cover layer in direct contact with the material) of the conveyor belts used in high-temperature environments. However, the tensile strength of the ethylene-propylene rubber is significantly lower than that of the substituted styrene-butadiene rubber or natural rubber. Particularly, the defect of low strength becomes more obvious when a large amount of ethylene propylene monomer (EPM) is used to satisfy better heat resistance. Therefore, the use of ethylene-propylene rubber as a cover rubber for heat-resistant conveyor belts limits the scope of application of such heat-resistant conveyor belts.\n\nChinese Patent Publication No.",
  "cpc": [
    "C08L 23/16",
    "B29D 29/00",
    "B29D 29/06",
    "B65G 15/32",
    "C08K 13/02",
    "C08K 2003/0893",
    "C08K 2003/222",
    "C08K 2003/2296",
    "C08K 2003/265",
    "C08K 2003/267",
    "C08K 3/04",
    "C08K 3/06",
    "C08K 3/22",
    "C08K 3/346",
    "C08K 5/01",
    "C08K 5/09",
    "C08K 5/14",
    "C08K 5/3492",
    "C08L 2201/08",
    "C08L 2205/025",
    "C08L 2205/03",
    "C08L 2205/035",
    "C08L 2207/066",
    "C08L 23/06",
    "C08L 23/08",
    "C08L 23/0815",
    "C08L 2312/00"
  ],
  "ipc": [
    "B29D 29/06",
    "B65G 15/32",
    "C08K 13/02",
    "C08K 3/04",
    "C08K 3/06",
    "C08K 3/08",
    "C08K 3/22",
    "C08K 3/26",
    "C08K 3/34",
    "C08K 5/01",
    "C08K 5/09",
    "C08K 5/14",
    "C08K 5/3492",
    "C08L 23/06",
    "C08L 23/08",
    "C08L 23/16"
  ],
  "assignees": [
    "Shaoxing Pinghe New Material Technology Co Ltd",
    "Hangzhou Xinglu Technology Co Ltd"
  ],
  "inventors": [
    "Tao Xu",
    "Zhi Sheng FU",
    "An Yang WU"
  ],
  "filing_date": "2018-01-12",
  "publication_date": "2024-12-24",
  "grant_date": "2024-12-24",
  "priority_date": "2017-01-13",
  "application_number": "US-201816477621-A",
  "family_id": "62868422",
  "cited_by_count": 3,
  "citations": [
    "US3645992A",
    "EP0050962A1",
    "US6103658A",
    "US6660677B1",
    "US6433080B1",
    "WO2003018078A1",
    "CN101028888A",
    "CN101531725A",
    "CN101812145A",
    "US20140287178A1",
    "CN103975013A",
    "CN102827312A",
    "CN102898730A",
    "CN105713301A",
    "WO2015122495A1",
    "US20160355622A1",
    "CN103980596A",
    "CN104312018A",
    "CN104926962A",
    "CN105017658A",
    "US11479661B2",
    "US11634566B2",
    "CN107556577A"
  ]
}